常用工程塑料和PVC塑料的密度表
常用塑料的密度(g/cm3)
材料 密度 材料 密度
PP 0.89~0.93 PA6-GF20 1.22~1.28
PP-T10 0.95~0.99 PA6-GF30 1.33~1.40
PP-T20 1.03~1.07 PA6-GF35 1.38~1.44
PP-T30 1.10~1.14 PA6-GF40 1.40~1.46
PP-T40 1.19~1.25 PA6-GF50 1.54~1.60
PP-GF20 1.10~1.14 PA6-(GF10+M20) 1.33~1.41
PP-GF30 1.12~1.18 PA6-(GF15+M25) 1.40~1.52
PP-GF40 1.19~1.25 PA6-M30 1.30~1.44
PP-LGF20 1.02~1.06 PA66 1.12~1.16
PP-LGF30 1.10~1.14 PA66-GF15 1.20~1.26
PP-LGF40 1.19~1.25 PA66-GF20 1.24~1.30
GMT-20 1.02~1.08 PA66-GF30 1.33~1.39
GMT-30 1.07~1.17 PA66-GF35 1.36~1.44
GMT-40 1.17~1.27 PA66-GF40 1.43~1.51
PP-EPDM 0.86~1.92 PA66-GF45 1.45~1.55
PP-EPDM-T10 0.94~1.00 PA66-GF50 1.51~1.61
PP-EPDM-T15 1.00~1.04 PA66-GF55 1.59~1.69
PP-EPDM-T20 1.03~1.07 PA66-GF60 1.67~1.77
PP-EPDM-T25 1.07~1.11 PA66-M40 1.46~1.54
PP-EPDM-T30 1.10~1.16 PA11 1.03~1.06
LDPE 0.91~0.94 PA12 1.00~1.06
HDPE 0.93~0.97 PA46 1.16~1.20
POM 1.40~1.44 PA46-GF30 1.38~1.44
PPO 1.03~1.07 PA46-GF40 1.47~1.53
PPO+PA 1.06~1.10 PA612 1.05~1.07
PBT 1.30~1.35 PA6/6T 1.13~1.19
PBT+GF10 1.40~1.45 PA6/6T-GF30 1.33~1.41
PBT+GF20 1.45~1.50 PA66/6T 1.12~1.18
PBT+GF30 1.50~1.55 PA66/6T-GF30 1.44~1.52
PBT/PET-T20 1.47~1.53 PA66/6T-M30 1.44~1.49
PET-GF20 1.47~1.53 PA-MXDD6(PAA)-GF30 1.39~1.47
PET-GF30 1.54~1.62 PMMA 1.17~1.20
PET-GF40 1.63~1.73 PC 1.18~1.22
PA6 1.12~1.15 PC-HT 1.12~1.20
PA6-GF15 1.20~1.26 PAR 1.20~1.26
ABS 1.04~1.08 PPS-(GF+MD)65 1.90~2.01
AES 1.02~1.06 PSU 1.21~1.27
ASA 1.06~1.09 PSU-GF30 1.48~1.56
PC+ABS 1.10~1.16 LCP-GF30 1.58~1.66
PC+ASA 1.12~1.18 LCP-M30 1.59~1.67
PC+PBT 1.18~1.23 PES 1.34~1.40
PS 1.03~1.07 PES-GF30 1.50~1.56
PA+ABS 1.04~1.10 PEI 1.24~1.30
TPS 0.9~1.2 PI 1.35~1.41
TPO 0.9~1.05 PEEK 1.27~1.33
TPV 0.95~1.0 PEEK-GF30 1.46~1.54
TPU 1.05~1.25 PEEK-CF30 1.37~1.43
TPC 1.15~1.4 PTFE 2.12~2.17
TPA 1.0~1.15
PPS 1.33~1.39
PPS-GF40 1.62~1.70

公司简介|新闻中心|产品中心|操作视频|技术文章|售后服务|联系我们

Copyright @ 2010-2012 All Rights Reserved版权所有:厦门雄发仪器仪表有限公司:闽ICP11014722号  Tel:0592-5187269  QQ:958747345
橡胶密度计,比重计,橡胶密度测试仪,塑料比重计,PVC密度仪,密度天平,液体比重计,粉末密度测试仪

页面执行时间 0.04688 秒

分享到:
分享按钮